Due to the hard carbon nanofibers and abundant welded joints among the nanofibers, the hard carbon aerogels display robust and stable mechanical performances, including super-elasticity, high strength, extremely fast recovery speed (860 mm s-1) and low energy loss coefficient (<0.16). After tested under 50 % strain for 104 cycles, the carbon aerogel shows only 2 % plastic deformation, and retained 93 % original stress.

The polymerization of resin monomers was initiated in the presence of nanofibers as structural templates to prepare a hydrogel with nanofibrous networks, followed by the drying and pyrolysis to get hard carbon aerogel. During polymerization, the monomers deposit on templates and weld the fiber-fiber joints, leaving a random network structure with massive robust joints. Moreover, physical properties (such as diameters of nanofiber, densities of aerogels, and mechanical properties) can be controlled by simply tuning templates and the amount of raw materials.